| Cladding Material: | B171 C46400 | Base Material: | A516 Gr.70 |
|---|---|---|---|
| Size: | (10+120)*OD1530mm | Max. Size: | 28sqm |
| Production Code: | ASTM B432, ASME SB432 | Surface Treatment: | Auto Polished |
120mm thickness Copper Clad Plate / Tubesheet for Heat Exchangers
Quick Product Details
B171 C46400/SA516 Gr.70 Thick Copper Clad Plate (Tubesheet) for Heat Exchangers
Explosion bonded / Naval brass clad plate / B 171 C46400 clad
Cladding metal thickness:10mm
Base metal thickness: 120mm
Size: (10+120)*OD1530mm
Drilling: as per drawing
Packing: plywood case packing
Table for available type of Copper/Naval brass clad plates:
|
Product Names: |
Copper (Naval Brass) Clad Plate/Sheet, Copper (Naval Brass) Clad Tube Sheet/ Tube Plate |
|||
|
Production Codes: |
ASTM B432, ASME SB432, DIN , BS, JIS, GB/T, ISO, etc. |
|||
|
Copper Grades: |
C10100, C10200, C11000, C26200, C28000, C46400, C70600, C71500, etc. |
|||
|
Form |
Description |
Base Layer |
Base Layer Grade |
Maximum Size |
|
Clad Plate |
Copper (Naval Brass) / Carbon Steel Clad |
Carbon steel plate and forging |
SA516 Gr.60(N),Gr.70(N),SA387 Gr.11, Gr.22, SA266, SA350, etc. |
(1.5~14)/(2~200) x W(max W 4110) x L(max L 7000) |
|
Copper (Naval Brass)/ Stainless Steel (Duplex) Clad |
Duplex, Stainless Steel & their forgings |
304L,316L, 316Ti, 321, 317L, 310S, 410S, 904L, 1805, 2205, 2507, Al6XN, 254sMo,etc. |
(1.5~14)/(2~200) x W(max W 4110) x L(max L 7000) |
|
|
Titanium / Copper (Naval Brass) Clad |
Titanium |
ASTM/ASME B265 Gr1, Gr2, Gr.3, Gr.5, Gr7, Gr.9, Gr12 |
(1.5~14)/(2~100) x W(max W 2100) x L(max L 6000) |
|
|
Copper (Naval Brass)/ Aluminum Clad |
Aluminum |
A1050, A1060, A1070, A1100, A5052, etc. |
(1.5~14)/(6~50) x W(max W 1500) x L (max L 1500) |
|
|
Copper (Naval Brass)/ Nickel Clad |
Nickel and its alloy |
N02200, Monel 400, Inconel 600, Incoloy 800, 825, C276, C22, etc |
(1.5~14)/(6~50) x W(max W 2000) x L (max L 5000) |
|
|
Copper (Naval Brass)/ Carbon Steel / Copper Clad |
Carbon steel plate and forging |
SA516 Gr.60(N),Gr.70(N),SA387 Gr.11, Gr.22, SA266, SA350, etc. |
(1.5~14)/(6~200)/(1~10) x W(max W 3000) x L(max L 4000) |
|
|
Copper / Titanium / Copper Clad |
Titanium |
ASTM/ASME B265 Gr1, Gr2, Gr.3, Gr.5, Gr7, Gr.9, Gr12 |
(1.5~14)/(2~100) x W(max W 2100) x L(max L 4000) |
|
|
Copper (Naval Brass)/ Carbon Steel / Stainless Steel Clad |
Carbon steel plate and forging |
SA516 Gr.60(N),Gr.70(N),SA387 Gr.11, Gr.22, SA266, SA350, etc. |
(1.5~14)/(6~200)/(1.5~10) x W(max W 4110) x L(max L 4000) |
|
|
Duplex, Stainless Steel & their forgings |
304L,316L, 316Ti, 321, 317L, 310S, 410S, 904L, 1805, 2205, 2507, Al6XN, 254sMo,etc. |
|||
|
Aluminum / Copper / Carbon Steel Clad |
Aluminum |
A1050, A1060, A1070, A1100, A5052, etc. |
(1.5~40)/(1-5)/(8~200) x W(max W 1000) x L(max L 1000) |
|
|
Carbon steel plate and forging |
SA516 Gr.60(N),Gr.70(N),SA387 Gr.11, Gr.22, SA266, SA350, etc. |
|||
|
Aluminum / Copper (Naval Brass)/ Aluminum Clad |
Aluminum |
A1050, A1060, A1070, A1100, A5052, etc. |
(1.5~40)/(1-5)/(1~100) x W(max W 1000) x L(max L 1000) |
|
Description:
Explosion welding is a solid state joining process in which explosive energy is used to propel the component metal parts together to form a metallurgical bond. At the point of impact of the two components, a thin layer is stripped from both colliding surfaces and is ejected as a molten metal jet. This jet contains the surface contaminants and oxides that would otherwise prevent bonding. The two surfaces are in intimate contact under extreme pressure enabling the bond to be formed.
Applications:
Petro-chemical, Vacuum Salt Industry, Chlor-alkali, Metallurgical, Food, Light Industry, Medicine, Auto Industry, Electrolytic Aluminum, Fertilizer, Power Industry, Building Materials, Electrolysis Industry, Hydrometallurgy etc.
Competitive Advantage:
1. Abundant experience in non-ferrous metal cladding and production.
With more than one decade of abundant experience in non-ferrous metal cladding and production, we provide high quality explosion bonded clad plates and clad heads with the cladding layer made of Nickel Alloy, Titanium Alloy, Copper-Nickel Alloy, Zirconium, Tantalum Alloy, Super Stainless Steel, aluminum and other materials according to ASTM, ASME, JIS, DIN, ISO other codes. More than 20 items of inventory or practical new-type patents also provide us with strong research and technical supports for our products.
2. Professional technical consulting service provides you with assistance.
- Generate technical specification to adopt in local market
- Technical bid evaluation and clarification
- Supplier technical document review, such as inspection and test plan, WPS / PQR, fabrication procedures, etc.
- Technical consulting on material, welding, NDE, etc.
- Non-conformance solution consulting
- Others that might be requested by customer
3. Independent inspection service covers following activities.
- Technical clarification with customer
- Attend / organize pre-inspection meeting
- In-process inspection, including: Material inspection, Test witness, Visual & dimensional inspection, Welding inspection, NDE inspection, Coating inspection
- Final inspection on finished products
- Packing inspection
- Progress report and schedule expediting
- Other inspection might be requested by customer
4. Transportation advantage
Located close to Shanghai seaport, we enjoy shipment convenience for large-sized explosion bonded clad plates and heads.